304 stainless steel sheets stockist Price cut
Product Description | stainless steel sheet |
Grade | 304 321 316L 309S 310S 201 202 |
standared | JIS, AISI, ASTM, GB, DIN,SUS |
Thickness | 0.4mm 0.5mm 0.6mm 0.7mm 0.8mm 0.9mm 1.0mm 1.2mm 1.5mm 2.0mm2.5mm 3.0mm--12mm |
SIZE | 1000*2000/1219*2438/1250*2500/1500*6000 or as the customer requirest |
Surface finish | 2B, BA, Hair Line, No.1,No.4, Mirror Finish |
Application | chemical, metallurgy, boiler |
Contacts | If you have any question, please contact us with mile, msn or telephone. |
Product Packing | Export standard package :bundled wooden box or be required; The inner size of container is below: 20 ft GP:5.8m(length)x 2.13m(width)x 2.18m(high) about 24-26 CBM 40 ft GP:11.8m(length)x 2.13m(width)x 2.72m(high)about 68 CBM We will packing as the factory ,and reach the stander of export . Or as the customer request.In addition,We will make the products with good surface protection. |
Delivery time | within 30 days after we got your 30% deposit |
Payment | 30% deposit by after s igned this contect. The balance payment by T/T after got the faxed B/L |
Attention | We are the agent of TISCO in north, China. And we have the best and the longest contect relation with JISCO, BISCO,KSK, and KRUPP. We can also produce the stainless steel sheet,bar, pipe,tube ...which is unstandared. We will give you the bottom price and the fastest speed and then give you the satisfied service for you |
304 stainless steel sheets stockist Price cut
304 Stainless Steel sheet
Stainless steel 304 is an austenitic grade that can be severely deep drawn. This property has resulted in 304 being the dominant grade used in applications like sinks and saucepans.
Chemical Composition of Stainless Steel 304 | ||||||||||||||||||||||||||||||||||||||
Table 1. Typical chemical composition for 304 stainless steel alloys
| ||||||||||||||||||||||||||||||||||||||
Properties of Stainless Steel 304 | ||||||||||||||||||||||||||||||||||||||
Mechanical Properties of Stainless Steel 304 Table 2. Typical mechanical properties for 304 stainless steel alloys
Physical Properties of Stainless Steel 304 Table 3. Typical physical properties for 304 stainless steel alloys
|
Corrosion Resistance of Stainless Steel 304
Stainless steel 304 has excellent corrosion resistance in a wide variety of environments and when in contact with different corrosive media. Pitting and crevice corrosion can occur in environments containing chlorides. Stress corrosion cracking can occur at temperatures over 60°C.
Heat Resistance of Stainless Steel 304
Stainless steel 304 has good resistance to oxidation in intermittent service up to 870°C and in continuous service to 925°C. However, continuous use at 425-860°C is not recommended if corrosion resistance in water is required. In this instance 304L is recommended due to its resistance to carbide precipitation.
Where high strength is required at temperatures above 500°C and up to 800°C, grade 304H is recommended. This material will retain aqueous corrosion resistance.
Fabrication of Stainless Steel 304
Fabrication of all stainless steels should be done only with tools dedicated to stainless steel materials. Tooling and work surfaces must be thoroughly cleaned before use. These precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.
Cold Working of Stainless Steel 304
Stainless steel 304 readily work hardens. Fabrication methods involving cold working may require an intermediate annealing stage to alleviate work hardening and avoid tearing or cracking. At the completion of fabrication a full annealing operation should be employed to reduce internal stresses and optimise corrosion resistance.
Hot Working of Stainless Steel 304
Fabrication methods, like forging, that involve hot working should occur after uniform heating to 1149-1260°C. The fabricated components should then be rapidly cooled to ensure maximum corrosion resistance.
Heat Treatment of Stainless Steel 304
Stainless steel 304 cannot be hardened by heat treatment.
Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C.
Machinability
Stainless steel 304 has good machinability. Machining can be enhanced by using the following rules:
Cutting edges must be kept sharp. Dull edges cause excess work hardening. Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material. Chip breakers should be employed to assist in ensuring swarf remains clear of the work Low thermal conductivity of austenitic alloys results in heat concentrating at the cutting edges. This means coolants and lubricants are necessary and must be used in large quantities.Welding of Stainless Steel 304
Fusion welding performance for Stainless steel 304 is excellent both with and without fillers. Recommended filler rods and electrodes for stainless steel 304 is grade 308 stainless steel. For 304L the recommended filler is 308L. Heavy welded sections may require post-weld annealing. This step is not required for 304L. Grade 321 may be used if post-weld heat treatment is not possible.
Applications of Stainless Steel 304
Stainless steel 304 is typically used in:
Sinks and splashbacks Saucepans Cutlery and flatware Architectural panelling Sanitaryware and troughs Tubing Brewery, dairy, food and pharmaceutical production equipment Springs, nuts, bolts and screws304 stainless steel sheets stockist Price cut